Progressive fracture of [0/90/± θ]S composite structure under uniform pressure load
Δεν υπάρχει διαθέσιμη μικρογραφία
Ημερομηνία
2008
Τίτλος Εφημερίδας
Περιοδικό ISSN
Τίτλος τόμου
Εκδότης
Δικαιώματα
Attribution-NonCommercial-NoDerivatives 4.0 Διεθνές
Άδειες
Παραπομπή
Παραπομπή
Περίληψη
S-Glass/epoxy [0/90/ ± θ]S for θ=45°, 60° and 75° laminated fiber-reinforced composite stiffened plate was simulated to investigated
for damage and fracture progression under uniform pressure. An integrated computer code was augmented for the simulation of the
damage initiation, growth, accumulation, and propagation to fracture and to structural collapse. Results show in detail the damage progression
sequence and structural fracture resistance during different degradation stages. Damage through the thickness of the laminate initiated first at [0/90/ ± 45]S at 15.168 MPa (2200 psi), followed by [0/90/ ± 60]S at 16.96 MPa (2460 psi) and finally by [0/90/ ± 75]S at 19.3 MPa (2800 psi). After damage initiation happened the cracks propagate rapidly to structural fracture.